Semiconductor structure and manufacturing method thereof

ABSTRACT

Provided are a semiconductor structure and a manufacturing method thereof. The manufacturing method includes the following steps. A substrate having a capacitor region and a periphery region is provided, wherein a transistor is formed in the substrate in the capacitor region, and a conductive device is formed in the substrate in the periphery region. A capacitor is formed on the substrate in the capacitance region, wherein the capacitor is electrically connected to the transistor, and an upper electrode layer of the capacitor extends onto the substrate in the periphery region. A protective layer is formed on the upper electrode layer. A doped layer is formed in at least the surface of the protective layer in the capacitor region. An etching process is performed using the doped layer as a mask to remove the protective layer and the upper electrode layer in the periphery region.

CROSS-REFERENCE TO RELATED APPLICATION

This application claims the priority benefit of Taiwan application serial no. 109129814, filed on Sep. 1, 2020. The entirety of the above-mentioned patent application is hereby incorporated by reference herein and made a part of this specification.

BACKGROUND Technical Field

The invention relates to a semiconductor structure and a manufacturing method thereof.

Description of Related Art

In a memory structure, a memory array is disposed in a cell region as a storage device. In addition, other electronic devices are disposed in a periphery region outside the cell region, and a voltage is applied to the electronic devices through contacts connected to the electronic devices.

Generally speaking, in the process of forming a metal-insulator-metal (MIM) capacitor, a lower electrode and an insulating layer are sequentially defined on a substrate, and then a metal layer is formed on the substrate. Then, a patterning process is performed on the metal layer to define an upper electrode. In the above patterning process, a photoresist layer is used to define the pattern of the upper electrode, and then an anisotropic etching process is performed to remove the metal layer not covered by the photoresist layer. However, in order to ensure that the formed upper electrode can completely overlap the insulating layer and the lower electrode, the photoresist layer not only covers the metal layer in the capacitor region, but also covers the metal layer adjacent to the capacitor region in the periphery region to prevent the metal layer in the capacitor region from being removed during etching.

However, the above method causes the formed upper electrode to extend into the periphery region. Since the contacts in the periphery region must be spaced a certain distance from the upper electrode extending into the periphery region to prevent short circuits, the area of the periphery region increases, which leads to an increase in chip size.

SUMMARY

The present invention provides a semiconductor structure and a manufacturing method thereof, in which the upper electrode of the capacitor in the capacitor region does not extend into the periphery region.

A semiconductor structure of the present invention includes a substrate having a capacitor region and a periphery region, and a capacitor. A transistor is disposed in the substrate in the capacitor region, and a conductive device is disposed in the substrate in the periphery region. The capacitor is disposed on the substrate in the capacitor region and electrically connected to the transistor, wherein an upper electrode layer of the capacitor does not extend into the periphery region.

A manufacturing method of the semiconductor structure of the present invention includes the following steps. A substrate having a capacitor region and a periphery region is provided, wherein a transistor is formed in the substrate in the capacitor region, and a conductive device is formed in the substrate in the periphery region. A capacitor is formed on the substrate in the capacitance region, wherein the capacitor is electrically connected to the transistor, and an upper electrode layer of the capacitor extends onto the substrate in the periphery region. A protective layer is formed on the upper electrode layer. A doped layer is formed in at least the surface of the protective layer in the capacitor region. An etching process is performed using the doped layer as a mask to remove the protective layer and the upper electrode layer in the periphery region.

Based on the above, in the manufacturing method of the semiconductor structure of the present invention, since the upper electrode layer in the periphery region has been completely removed, the position of the subsequently formed contact can be as close as possible to the capacitor in the capacitor region without being in contact with the capacitor. In this way, the distance between the contact and the capacitor region (or capacitor) can be minimized, and therefore the purpose of reducing the size of the chip can be achieved.

To make the aforementioned more comprehensible, several embodiments accompanied with drawings are described in detail as follows.

BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings are included to provide a further understanding of the disclosure, and are incorporated in and constitute a part of this specification. The drawings illustrate exemplary embodiments of the disclosure and, together with the description, serve to explain the principles of the disclosure.

FIGS. 1A to 1G are schematic cross-sectional views of a manufacturing process of a semiconductor structure according to an embodiment of the present invention.

DESCRIPTION OF THE EMBODIMENTS

The embodiments are described in detail below with reference to the accompanying drawings, but the embodiments are not intended to limit the scope of the present invention. In addition, the drawings are for illustrative purposes only and are not drawn to the original dimensions. For the sake of easy understanding, the same elements in the following description will be denoted by the same reference numerals.

FIGS. 1A to 1G are schematic cross-sectional views of a manufacturing process of a semiconductor structure according to an embodiment of the present invention.

Referring to FIG. 1A, a substrate 100 is provided. In this embodiment, the substrate 100 is a dielectric substrate, which is, for example, a dielectric layer formed on a silicon substrate and covering electronic devices (such as transistors) disposed on the silicon substrate. The substrate 100 has a capacitor region 100 a and a periphery region 100 b. In this embodiment, in order to make the diagram clear, the above-mentioned silicon substrate and the electronic devices disposed thereon are not shown. The capacitor region 100 a is a region for disposing the capacitor, and the capacitor is electrically connected to the transistor on the silicon substrate to form a dynamic random access memory (DRAM). The periphery region 100 b is a region for disposing various electronic devices and circuit patterns, which is well known to those skilled in the art and will not be further described here.

Next, a conductive layer 102 is formed on the substrate 100 in the capacitor region 100 a. The conductive layer 102 is, for example, a metal layer or a composite layer composed of a metal layer and a metal nitride layer, but the invention is not limited thereto. The conductive layer 102 is used as the bottom electrode of the capacitor. Then, a dielectric layer 104 is formed on the conductive layer 102. In this embodiment, the dielectric layer 104 only covers the surface of the conductive layer 102, but the invention is not limited thereto. In other embodiments, the dielectric layer 104 may also extend onto the surface of the substrate 100 in the periphery region 11 b. The material of the dielectric layer 104 is, for example, a dielectric material having a high dielectric constant. For example, the dielectric layer 104 may be a composite layer composed of a zirconium oxide (ZrO₂) layer, an aluminum oxide (Al₂O₃) layer and a zirconium oxide layer, but the present invention is not limited thereto. The dielectric layer 104 is used as a capacitor dielectric layer of the capacitor. After that, a conductive layer 106 is conformally formed on the substrate 100. Therefore, in addition to being located in the capacitor region 100 a, the conductive layer 106 will also extend onto the substrate 100 in the periphery region 100 b. The conductive layer 106 is, for example, a metal layer or a composite layer composed of a metal layer and a metal nitride layer, but the invention is not limited thereto. The conductive layer 106 is used as the upper electrode of the capacitor. In this embodiment, the conductive layer 102, the dielectric layer 104 and the conductive layer 106 in the capacitor region 100 a constitute the capacitor 108, and the conductive layer 102 (lower electrode) is electrically connected to the above-mentioned transistor on the silicon substrate by the contact (not shown) in the substrate 100.

Referring to FIG. 1B, a protective layer 110 is formed on the conductive layer 106 (upper electrode). In this embodiment, the protective layer 110 is, for example, an oxide layer, but the invention is not limited thereto. The protective layer 110 is used to protect the conductive layer 106 to prevent the conductive layer 106 from being oxidized due to contact with the external environment in the subsequent process. Next, a dielectric layer 112 is formed on the protective layer 110. In this embodiment, the thickness of the dielectric layer 112 in the periphery region 100 b is greater than the thickness of the dielectric layer 112 in the capacitor region 100 a. It can be clearly seen from FIG. 1B that only a thin dielectric layer 112 is formed on the protective layer 110 in the capacitor region 100 a after forming the dielectric layer 112. In one embodiment, the thickness of the dielectric layer 112 in the periphery region 100 b is more than twice the thickness of the dielectric layer 112 in the capacitor region 100 a. In order to form the dielectric layer 112 with the above-mentioned thickness characteristics, in this embodiment, a spin coating process is performed to form the dielectric layer 112. Based on the characteristics of the spin coating process, a portion of dielectric layer 112 with a larger thickness may be formed in the periphery region 100 b and a portion of the dielectric layer 112 with a smaller thickness may be formed on the capacitor 108 in the capacitor region 100 a without special adjustment of process parameters.

In addition, the dielectric layer 112 and the protective layer 110 must have etching selectivity. In other words, during the etching process, the etching rate of the dielectric layer 112 must be greater than the etching rate of the protective layer 110. In one embodiment, the dielectric layer 112 may be an oxide layer, and during the etching process, the etching rate of the dielectric layer 112 is greater than the etching rate of the protective layer 110.

Referring to FIG. 1C, the dielectric layer 112 in the capacitor region 100 a is removed to expose the protective layer 110 on the top surface of the capacitor 108. The method of removing the dielectric layer 112 in the capacitor region 100 a is, for example, an anisotropic etching process. In the process of removing the dielectric layer 112 in the capacitor region 100 a, the dielectric layer 112 in the periphery region 100 b is also removed at the same time. Since the thickness of the dielectric layer 112 in the periphery region 100 b is greater than the thickness of the dielectric layer 112 in the capacitor region 100 a, after the dielectric layer 112 in the capacitor region 100 a is completely removed, the dielectric layer 112 still remains in the periphery region 100 b.

Referring to FIG. 1D, a doped layer 114 is formed on the surface of the protective layer 110 in the capacitor region 100 a to change the etching characteristics of the protective layer 110. The method of forming the doped layer 114 is, for example, an implantation process. The dopants implanted in the above implantation process are, for example, silicon, germanium, arsenic or a combination thereof, but the present invention is not limited thereto. In this embodiment, during the implantation process, in addition to being implanted into the surface of the protective layer 110, the dopants are also implanted into the surface of the dielectric layer 112 to form the doped layer 116, but the invention is not limited thereto. In other embodiments, the dopants may also be implanted only in the protective layer 110.

In this embodiment, the doped layer 114 and the protective layer 110 have etching selectivity. In other words, during the etching process, the etching rate of the doped layer 114 is less than the etching rate of the protective layer 110, so as to serve as an etching mask on the protective layer 110.

In addition, in this embodiment, the doped layer 114 is only formed in the surface of the protective layer 110, but the invention is not limited thereto. In other embodiments, the doped layer 114 may also be formed in the entire protective layer 110, that is, the depth of the doped layer 114 is the thickness of the protective layer 110.

Referring to FIG. 1E, the remaining dielectric layer 112 is removed to expose the protective layer 110 in the periphery region 110 b. The method of removing the dielectric layer 112 is, for example, an ash trip process. In this embodiment, since the doped layer 114 is formed in the surface of the protective layer 110, the protective layer 110 in the capacitor region 110 a may be prevented from being removed during the process of removing the dielectric layer 112.

Referring to FIG. 1F, using the doped layer 114 as a mask, an etching process is performed to remove the protective layer 110 in the periphery region 100 b, and expose the conductive layer 106 in the periphery region 100 b. In this embodiment, the etching process is, for example, an isotropic etching process. In this embodiment, based on the characteristics of the isotropic etching process, in addition to removing the protective layer 110 in the periphery region 100 b that is not covered by the doped layer 114, the protective layer 110 located at the boundary between the capacitor region 100 a and the peripheral region 100 b (that is, on the sidewall of the capacitor 108) may also be removed. In addition, depending on the time of the etching process, the slight doped layer 114 located at the boundary between the capacitor region 100 a and the periphery region 100 b may also be removed.

Referring to FIG. 1G, using the doped layer 114 as a mask, an etching process is performed to remove the conductive layer 106 in the periphery region 100 b to expose the substrate 100. In this embodiment, the etching process is, for example, an anisotropic etching process. Since the doped layer 114 is only formed in the capacitor region 100 a, the conductive layer 106 in the periphery region 110 b can be completely removed. In addition, in this embodiment, the doped layer 114 is used as a mask to perform the etching process, so there is no need to additionally form a photoresist layer covering the capacitor region 100 a. After that, the following well-known process may be performed. For example, a dielectric layer 118 covering the capacitor region 100 a and the periphery region 110 b is formed on the substrate 100, and a contact 120 connected to a conductive device (not shown) in the substrate 100 is formed in the dielectric layer 118.

In this embodiment, since the conductive layer 106 in the periphery region 110 b has been completely removed, the position of the contact 120 may be as close as possible to the capacitor 108 without being in contact with the capacitor 108. In other words, the distance D between the contact 120 and the capacitor region 100 a (or the capacitor 108) may be minimized, thereby achieving the purpose of reducing the chip size.

The semiconductor structure of the present invention will be described below by taking FIG. 1G as an example. Referring to FIG. 1G, the semiconductor structure of the present invention includes a substrate 100 and a capacitor 108. The capacitor 108 is disposed on the substrate 100 in the capacitor region 100 a and is electrically connected to a transistor (not shown) in the substrate 100. In addition, the conductive layer 106 as the upper electrode of the capacitor 108 does not extend into the periphery region 100 b. The semiconductor structure of the present invention may further include a contact 120 disposed in the periphery region 100 b and electrically connected to a conductive device (not shown) in the substrate 100. Since the upper electrode (conductive layer 106) of the capacitor 108 does not extend into the periphery region 100 b, the position of the contact 120 may be as close as possible to the capacitor 108 without being in contact with the capacitor 108. That is, the distance D between the contact 120 and the capacitor region 100 a (or capacitor 108) may be minimized to achieve the purpose of reducing the chip size.

In the above embodiment, the capacitor 108 including the conductive layer 102 (lower electrode), the dielectric layer 104 (capacitor dielectric layer) and the conductive layer 106 (upper electrode) is a flat capacitor well known to those skilled in the art, but the present invention does not limited thereto. In other embodiments, the capacitor 108 may be other types of capacitors, such as a cup-shaped capacitor, and the manufacturing method of the semiconductor structure with such capacitor is the same as that described in FIGS. 1A to 1G, and will not be further described here.

It will be apparent to those skilled in the art that various modifications and variations can be made to the disclosed embodiments without departing from the scope or spirit of the disclosure. In view of the foregoing, it is intended that the disclosure covers modifications and variations disposed that they fall within the scope of the following claims and their equivalents. 

What is claimed is:
 1. A manufacturing method of a semiconductor structure, comprising: providing a substrate, wherein the substrate has a capacitor region and a periphery region, a transistor is formed in the substrate in the capacitor region, and a conductive device is formed in the substrate in the periphery region; forming a capacitor on the substrate in the capacitor region, wherein the capacitor is electrically connected to the transistor, and an upper electrode layer of the capacitor extends onto the substrate in the periphery region; forming a protective layer on the upper electrode layer; forming a doped layer in at least the surface of the protective layer in the capacitor region; and performing an etching process using the doped layer as a mask to remove the protective layer and the upper electrode layer in the periphery region.
 2. The manufacturing method of claim 1, wherein a method of forming the doped layer comprises: forming a dielectric layer on the protective layer in the periphery region; performing an implantation process to implant dopants into at least the surface of the protective layer in the capacitor region; and removing the dielectric layer.
 3. The manufacturing method of claim 2, wherein a method of forming the dielectric layer comprises: forming a dielectric material layer on the protective layer, wherein the thickness of the dielectric material layer in the periphery region is greater than the thickness of the dielectric material layer in the capacitor region; and performing an anisotropic etching process to remove the dielectric material layer in the capacitor region.
 4. The manufacturing method of claim 3, wherein a method of forming the dielectric material layer comprises performing a spin coating process.
 5. The manufacturing method of claim 3, wherein the thickness of the dielectric material layer in the periphery region is more than twice the thickness of the dielectric material layer in the capacitor region.
 6. The manufacturing method of claim 2, wherein the dopants implanted in the implantation process comprise silicon, germanium, arsenic or a combination thereof.
 7. The manufacturing method of claim 1, wherein the doped layer is formed in the entire protective layer.
 8. The manufacturing method of claim 7, wherein a method of removing the protective layer and the upper electrode layer in the periphery region comprises: performing an isotropic etching process using the doped layer as a mask to remove the protective layer in the periphery region; and performing an anisotropic etching process using the doped layer as a mask to remove the upper electrode layer in the periphery region.
 9. The manufacturing method of claim 1, further comprising forming a contact electrically connected to the conductive device in the periphery region after removing the protective layer and the upper electrode layer in the periphery region.
 10. A semiconductor structure, comprising: a substrate, having a capacitor region and a periphery region, wherein a transistor is disposed in the substrate in the capacitor region, and a conductive device is disposed in the substrate in the periphery region; and a capacitor, disposed on the substrate in the capacitor region and electrically connected to the transistor, wherein an upper electrode layer of the capacitor does not extend into the periphery region.
 11. The semiconductor structure of claim 10, further comprising: a protective layer, disposed on the upper electrode layer of the capacitor; and a doped layer, disposed in at least the surface of the protective layer.
 12. The semiconductor structure of claim 11, wherein the doped layer is disposed in the entire protective layer.
 13. The semiconductor structure of claim 11, wherein the dopants in the doped layer comprise silicon, germanium, arsenic, or a combination thereof.
 14. The semiconductor structure of claim 10, further comprising a contact, disposed in the periphery region and electrically connected to the conductive device. 